Anycubic PC Filament 1kg – Translucent White

Engineering-grade PC filament | High impact and heat resistance | Smooth, lustrous surface finish | 1kg spool

The Anycubic PC Filament is an engineering-grade polycarbonate filament designed for makers and engineers who need parts that go beyond what standard PLA or ABS can offer. Compatible with FDM printers fitted with a nozzle of 0.2 mm or above, it prints at 270–290°C with a heated bed of 100–120°C, and supports print speeds of 40–250 mm/s. With a heat deflection temperature of 110°C and strong mechanical properties — including a tensile strength of 65±6 MPa and an Izod impact strength of 30±12 kJ/m² — it is well suited to structural parts, functional components, automotive applications, electronic housings, and outdoor use. The filament also delivers smooth model surfaces with a translucent, lustrous quality. Note that active drying is required before printing: 80°C for 8–12 hours. Supplied on a 1kg reusable spool with intelligent identification chip support for compatible Anycubic printers.

Features

• Engineering-grade PC filament for structural, functional, and outdoor applications
• Heat deflection temperature of 110°C — resists warping and deformation under prolonged heat
• Izod impact strength of 30±12 kJ/m² (X-Y) for tough, crack-resistant parts
• Tensile strength of 65±6 MPa and bending strength of 105±10 MPa
• Smooth, translucent, and lustrous surface finish
• Intelligent identification chip supported for compatible Anycubic printers
• Reusable spool with threaded connection system to reduce filament entanglement
• Active drying required before use: 80°C for 8–12 hours

Specifications

• Colour: Translucent White
• Dry Out Before Use: Required
• Drying Condition: 80 ℃, 8-12 h
• ACE Compatibility: Compatible
• Nozzle Size: Recommended 0.2 mm or above
• Printing Temperature: 270-290 ℃
• Heated Bed Temperature: 100-120 ℃
• Recommended Printing Speed: 40-250 mm/s
• Maximum Volume Speed (Flow Rate): 12 mm³/s
• Density: 1.2 g/cm³
• Melt Index: 15-20 g/10 min (270℃/1.2kg)
• Melting Point Temperature: 230 ℃
• Vicat Softening Temperature: 122 ℃
• Heat Deflection Temperature (0.45MPa): 110 ℃
• Young’s Modulus: 2550±100 MPa
• Tensile Strength: 65±6 MPa
• Elongation at Break: 9±4%
• Bending Modulus: 2900±150 MPa
• Bending Strength: 105±10 MPa
• lzod lmpact Strength (X-Y): 30±12 kJ/m²
• Tensile Strength (Z): 25±7 MPa
• Filament Type: Engineering filaments
• Recommend to Print: Structural parts, functional parts, automotive parts, outdoor use, electronic housing, artworks
• Intelligent Identification: Supported
• Reusable Filament Spool: Supported